RIGHT-POXY HIGH MOD GEL is a two part, 100% solids, low odor, 1:1 mix ratio, moisture insensitive epoxy resin compound with a non-sag, paste consistency.
• High Strength
• High Modulus
• Provides Load Transfer
• Virtually No Odor
• 1:1 Mix Ratio
• Outstanding Adhesion to Concrete
• Moisture Insensitive
• Non-Sag Paste
• Dowel Bar, Anchor Bolt & Re-Bar Adhesive
• Hardened Concrete Adhesive
• Vertical and Overhead Applications
• Rigid Pick-Proof Sealant for Windows, Doors, Joints, etc.
• Capseal for Crack Injection
• Repair Concrete Defects
RIGHT-POXY HIGH MOD GEL meets or exceeds the following standards:
ASTM C881-90, Type I, II, IV & V
Grade 3, Class B & C
AASHTO M-235
Concrete: The surface must be structurally sound, dry, free of grease, oils,
coatings, dust, Chemical Liquids and other contaminants. Surface laitance must be removed. The preferred method of surface preparation is abrasive blasting or other mechanical means. Oil contaminated surfaces should be degreased. Remove defective concrete, honeycombs, cavities, joint cracks, voids and other defects by routing to sound material. Following surface preparation, the cleaned surface should pull concrete when tested with a pull tester, or an elcometer (ASTM D4541).
Steel: All oils, greases, dirt, old coatings and chemical contaminants must be removed. The surface should be blasted to a near white metal finish (SSPC SP10) using clean dry aggregate.
Premix Part A and B with a slow speed motor and “Jiffy” mixer. Pour one part by volume of Part A and one part by volume of Part B into a clean, dry container and mechanically mix for 3-5 minutes. Scrape the sides and bottom of mixing container while mixing. Do not whip or aerate while mixing.
RIGHT-POXY HIGH MOD GEL Mortar: Gradually add clean, dry 20/40 mesh silica sand to mixed binder. Blend thoroughly. The mix ratio of aggregate to binder is approximately 1:1 by volume but may vary depending upon the desired consistency of the mortar.
Application and surface temperatures should be at least 40°F and rising.
Bonding hardened to hardened concrete: Apply mixed RIGHT-POXY HIGH
MOD GEL by spatula, brush or trowel. Ensure the surfaces to be joined have uniform coatings of RIGHT-POXY HIGH MOD GEL. For optimum results the bond line should not exceed 1/8 inch. Join surfaces and hold or clamp firmly. Ideally a small amount of adhesive should exude from the joint. Surfaces must be mated while the adhesive is still tacky.
Bonding anchor bolts, dowels, pins: RIGHT-POXY HIGH MOD GEL can be used neat or with an aggregate to anchor horizontal bolts. The anchor bolt hole should be free of all debris before gouting. The optimum hole size is 1/8” inch annular space or ¼” larger diameter than bar diameter. Depth of embedment is typically 10-15 times bolt diameter
Vertical and Overhead Repairs: Apply RIGHT-POXY HIGH MOD GEL neat as a scrub coat to the prepared concrete surface. Mix the RIGHT-POXY HIGH MOD GEL mortar epoxy mortar and apply to the area by trowel or spatula in lifts of 1 to 1½ inch. Allow each lift to reach initial set set before applying subsequent lifts.
Capseal & Set Ports for Pressure Injection: Place a small amount of the mixed RIGHT-POXY HIGH MOD GEL to the back of the port and carefully place over the crack. Be careful to not fill the hole of the injection port. Place neat mixed RIGHT-POXY HIGH MOD GEL to the cracks to be pressure injected and around each injection port. Allow sufficient cure time before pressure injection.
|
|
|
|
| |
|
|
Color, Part A |
Lt. Gray |
Color, Part B |
Tan |
Color (Mixed) |
Lt. Gray |
Solids, % |
100 |
Mixing Ratio (Parts A:B) by volume |
1:1 |
Pot Life, (2 gal unit), mins |
15-25 |
Gel Time, mins |
30 |
Consistency |
Non Sag Paste |
Compressive Stregth (ASTM D695), psi |
|
1 Day (neat resin), minimum |
8,000 |
7 Days (neat resin), minimum |
10,250 |
Compressive Modulus (ASTM D695), psi |
|
7 Days (neat resin) |
325,000 |
Compressive Strength (ASTM C109), psi |
|
7 Days (mortar) |
|
Tensile Properties (ASTM D638) |
|
Ultimate Strength @ 14 Days, psi |
7,050 |
Elongation at break, % |
2.5 |
Modulus, psi |
460,049 |
Bond Strength (ASTM C882), psi |
|
Hardened to Hardened Concrete |
|
2 Day (moist cure) |
2015 |
14 Days (moist cure) |
2236 |
14 Days (dry cure) |
3250 |
Heat Deflection Temp.(ASTM D648) |
124°F |
Water Absorption (ASTM D570) |
|
7 Day, 24 Hour Immersion, % |
0.31 |
For anchoring, 1 neat gal yields 231 cu.in. of grout. 1 gal neat RIGHT-POXY
HIGH MOD GEL with 1 gal dry 20/40 mesh silica sand will yield approximately
410 cu. in. of mortar. Coverage will vary depending on surface texture, porosity
and temperature.
Clean tools and application equipment immediately after use with methyl ethyl ketone, or xylene. Clean overspray or drips while still wet with solvent. Dried RIGHT-POXY HIGH MOD GEL will require mechanical abrasion for removal.
4 gallon case, 10 gal unit.
50° to 90°F (10° 32.2°C), protected from moisture.
2 years, unopened, proper storage.
For application procedures or surface conditions not specified above, please contact: Right Pointe Company 888-755-5700.
|
|
|
|